Patterning process and resist composition

ABSTRACT

A resist composition comprising a polymer comprising recurring units having an acid labile group of cyclopentyl with tert-butyl or tert-amyl pendant is coated onto a substrate, baked, exposed to high-energy radiation, PEB and developed in an organic solvent to form a negative pattern. A fine hole pattern can be formed from the resist composition with advantages including high dissolution contrast, good size control and wide depth of focus.

CROSS-REFERENCE TO RELATED APPLICATION

This non-provisional application claims priority under 35 U.S.C. §119(a) on Patent Application No. 2013-012870 filed in Japan on Jan. 28, 2013, the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

This invention relates to a pattern forming process comprising the steps of exposure of resist film, deprotection reaction with the aid of acid and heat, and development in an organic solvent to form a negative tone pattern in which the unexposed region is dissolved and the exposed region is not dissolved, and a resist composition used therein.

BACKGROUND ART

In the recent drive for higher integration and operating speeds in LSI devices, the pattern rule is made drastically finer. The photolithography which is currently on widespread use in the art is approaching the essential limit of resolution determined by the wavelength of a light source. As the light source used in the lithography for resist pattern formation, g-line (436 nm) or i-line (365 nm) from a mercury lamp was widely used in 1980's. Reducing the wavelength of exposure light was believed effective as the means for further reducing the feature size. For the mass production process of 64 MB dynamic random access memories (DRAM, processing feature size 0.25 μm or less) in 1990's and later ones, the exposure light source of i-line (365 nm) was replaced by a KrF excimer laser having a shorter wavelength of 248 nm. However, for the fabrication of DRAM with a degree of integration of 256 MB and 1 GB or more requiring a finer patterning technology (processing feature size 0.2 μm or less), a shorter wavelength light source was required. Over a decade, photolithography using ArF excimer laser light (193 nm) has been under active investigation. It was expected at the initial that the ArF lithography would be applied to the fabrication of 180-nm node devices. However, the KrF excimer lithography survived to the mass-scale fabrication of 130-nm node devices. So, the full application of ArF lithography started from the 90-nm node. The ArF lithography combined with a lens having an increased numerical aperture (NA) of 0.9 is considered to comply with 65-nm node devices. For the next 45-nm node devices which required an advancement to reduce the wavelength of exposure light, the F₂ lithography of 157 nm wavelength became a candidate. However, for the reasons that the projection lens uses a large amount of expensive CaF₂ single crystal, the scanner thus becomes expensive, hard pellicles are introduced due to the extremely low durability of soft pellicles, the optical system must be accordingly altered, and the etch resistance of resist is low; the development of F₂ lithography was stopped and instead, the ArF immersion lithography was introduced.

In the ArF immersion lithography, the space between the projection lens and the wafer is filled with water having a refractive index of 1.44. The partial fill system is compliant with high-speed scanning and when combined with a lens having a NA of 1.3, enables mass production of 45-nm node devices.

One candidate for the 32-nm node lithography is lithography using extreme ultraviolet (EUV) radiation with wavelength 13.5 nm. The EUV lithography has many accumulative problems to be overcome, including increased laser output, increased sensitivity, increased resolution and minimized edge roughness (LER, LWR) of resist film, defect-free MoSi laminate mask, reduced aberration of reflection mirror, and the like.

Another candidate for the 32-nm node lithography is high refractive index liquid immersion lithography. The development of this technology was stopped because LUAG, a high refractive index lens candidate had a low transmittance and the refractive index of liquid did not reach the goal of 1.8.

The process that now draws attention under the above-discussed circumstances is a double patterning process involving a first set of exposure and development to form a first pattern and a second set of exposure and development to form a pattern between the first pattern features. A number of double patterning processes are proposed. One exemplary process involves a first set of exposure and development to form a photoresist pattern having lines and spaces at intervals of 1:3, processing the underlying layer of hard mask by dry etching, applying another layer of hard mask thereon, a second set of exposure and development of a photoresist film to form a line pattern in the spaces of the first exposure, and processing the hard mask by dry etching, thereby forming a line-and-space pattern at a half pitch of the first pattern. An alternative process involves a first set of exposure and development to form a photoresist pattern having spaces and lines at intervals of 1:3, processing the underlying layer of hard mask by dry etching, applying a photoresist layer thereon, a second set of exposure and development to form a second space pattern on the remaining hard mask portion, and processing the hard mask by dry etching. In either process, the hard mask is processed by two dry etchings.

As compared with the line pattern, the hole pattern is difficult to reduce the feature size. In order for the prior art method to form fine holes, an attempt is made to form fine holes by under-exposure of a positive resist film combined with a hole pattern mask. This, however, results in the exposure margin being extremely narrowed. It is then proposed to form holes of greater size, followed by thermal flow or RELACS® method to shrink the holes as developed. However, there is a problem that control accuracy becomes lower as the pattern size after development and the size after shrinkage differ greater and the quantity of shrinkage is greater. With the hole shrinking method, the hole size can be shrunk, but the pitch cannot be narrowed.

It is then proposed in Non-Patent Document 1 that a pattern of X-direction lines is formed in a positive resist film using dipole illumination, the resist pattern is cured, another resist material is coated thereon, and a pattern of Y-direction lines is formed in the other resist film using dipole illumination, leaving a grid line pattern, spaces of which provide a hole pattern. Although a hole pattern can be formed at a wide margin by combining X and Y lines and using dipole illumination featuring a high contrast, it is difficult to etch vertically staged line patterns at a high dimensional accuracy. It is proposed in Non-Patent Document 2 to form a hole pattern by exposure of a negative resist film through a Levenson phase shift mask of X-direction lines combined with a Levenson phase shift mask of Y-direction lines. However, the crosslinking negative resist film has the drawback that the resolving power is low as compared with the positive resist film, because the maximum resolution of ultrafine holes is determined by the bridge margin.

A hole pattern resulting from a combination of two exposures of X- and Y-direction lines and subsequent image reversal into a negative pattern can be formed using a high-contrast line pattern of light. Thus holes having a narrow pitch and fine size can be opened as compared with the prior art.

Non-Patent Document 3 reports three methods for forming hole patterns via image reversal. The three methods are: method (1) involving subjecting a positive resist composition to two double-dipole exposures of X and Y lines to form a dot pattern, depositing a SiO₂ film thereon by LPCVD, and effecting O₂-RIE for reversal of dots into holes; method (2) involving forming a dot pattern by the same steps as in (1), but using a resist composition designed to turn alkali-soluble and solvent-insoluble upon heating, coating a phenol-base overcoat film thereon, effecting alkaline development for image reversal to form a hole pattern; and method (3) involving double dipole exposure of a positive resist composition and organic solvent development for image reversal to form holes.

The organic solvent development to form a negative pattern is a traditional technique. A resist composition comprising cyclized rubber is developed using an alkene such as xylene as the developer. An early chemically amplified resist composition comprising poly(tert-butoxycarbonyloxy-styrene) is developed with anisole as the developer to form a negative pattern.

Recently a highlight is put on the organic solvent development again. It would be desirable if a very fine hole pattern, which is not achievable with the positive tone, is resolvable through negative tone exposure. To this end, a positive resist composition featuring a high resolution is subjected to organic solvent development to form a negative pattern. An attempt to double a resolution by combining two developments, alkaline development and organic solvent development is under study.

As the ArF resist composition for negative tone development with organic solvent, positive ArF resist compositions of the prior art design may be used. Such pattern forming processes are described in Patent Documents 1 to 3. These patent documents disclose resist compositions for organic solvent development comprising a copolymer of hydroxyadamantane methacrylate, a copolymer of norbornane lactone methacrylate, and a copolymer of methacrylate having acidic groups including carboxyl, sulfo, phenol and thiol groups substituted with two or more acid labile groups, and pattern forming processes using the same.

Further, Patent Document 4 discloses a process for forming a pattern through organic solvent development in which a protective film is applied onto a resist film. Patent Document 5 discloses a topcoatless process for forming a pattern through organic solvent development in which an additive is added to a resist composition so that the additive may segregate at the resist film surface after spin coating to provide the surface with improved water repellency.

The positive development system involving deprotection reaction to generate a carboxyl group and subsequent neutralization reaction with aqueous alkaline developer to improve a dissolution rate achieves a high dissolution contrast in that the dissolution rate differs between the unexposed and exposed regions by a factor of more than 1,000. In contrast, the negative development system via organic solvent development provides a low contrast because the dissolution rate in the unexposed region due to solvation is low, and the dissolution rate thus differs between the unexposed and exposed regions by a factor of less than 100. For the negative development system via organic solvent development, it is desired to seek for a novel material which can offer a high dissolution contrast.

CITATION LIST

-   Patent Document 1: JP-A 2008-281974 -   Patent Document 2: JP-A 2008-281975 -   Patent Document 3: JP 4554665 -   Patent Document 4: JP 4590431 -   Patent Document 5: JP-A 2008-309879 -   Non-Patent Document 1: Proc. SPIE Vol. 5377, p. 255 (2004) -   Non-Patent Document 2: IEEE IEDM Tech. Digest 61 (1996) -   Non-Patent Document 3: Proc. SPIE Vol. 7274, p. 72740N (2009)

DISCLOSURE OF INVENTION

The organic solvent development is low in dissolution contrast, as compared with the positive resist system adapted to be dissolved in alkaline developer when deprotection reaction takes place to produce acidic carboxyl or phenol groups. Specifically, in the case of alkaline developer, the alkali dissolution rate differs more than 1,000 times between unexposed and exposed regions, whereas the difference in the case of organic solvent development is at most 100 times, and only about 10 times for certain materials. No sufficient margin is available. In the case of aqueous alkaline development, the dissolution rate is improved by neutralization reaction with carboxyl groups. In the case of organic solvent development with no accompanying reaction, the dissolution rate is low because dissolution is solely due to solvation. It is necessary not only to improve the dissolution rate of the unexposed region, but also to reduce the dissolution rate of the exposed region that is a remaining portion of resist film. If the dissolution rate of the exposed region is high, the thickness of the remaining film is so reduced that the underlying substrate may not be processed by etching through the pattern as developed. Further it is important to enhance the gradient or gamma (γ) at the dose corresponding to dissolution/non-dissolution conversion. A low γ value is prone to form an inversely tapered profile and allows for pattern collapse in the case of a line pattern. To obtain a perpendicular pattern, the resist must have a dissolution contrast having a γ value as high as possible.

While prior art photoresist compositions of the alkaline aqueous solution development type are described in Patent Documents 1 to 3, they have a low dissolution contrast upon organic solvent development. It would be desirable to have a novel material having a significant difference in dissolution rate between the exposed and unexposed regions and capable of achieving a high dissolution contrast (γ) upon organic solvent development.

When an attempt is made to form a hole pattern through negative development, regions surrounding the holes receive light so that excess acid is generated therein. Since the holes are not opened if the acid diffuses inside the holes, control of acid diffusion is also important.

An object of the invention is to provide a negative pattern-forming resist composition which has a significant dissolution contrast and a high sensitivity upon organic solvent development. Another object is to provide a pattern forming process capable of forming a hole pattern via positive/negative reversal by organic solvent development.

The inventors have found that a polymer comprising recurring units having an acid labile group of tertiary ester type, specifically an acid labile group of cyclopentyl having a tert-butyl or tert-amyl pendant group is effective as a base resin and that a resist composition comprising the polymer, when processed by exposure, PEB and organic solvent development, is improved in dissolution contrast.

When an acid labile group of such type is applied to a positive resist film subject to alkaline development, the high lipophilicity of branched alkyl pendant allows for swelling in developer and top bulging, giving rise to problems like pattern collapse, LWR degradation and bridging between pattern features. In negative pattern formation via organic solvent development, the branched alkyl pendant contributes to significant improvements in developer solubility and acid lability, leading to high dissolution contrast. Since the polymer is not swollen at all in organic solvent developer, the problems of pattern collapse or crush, bridge defects, and LWR degradation are eliminated. As a consequence, a fine hole pattern can be formed with advantages including high sensitivity, dimensional uniformity and wide depth of focus.

In one aspect, the invention provides a pattern forming process comprising the steps of:

applying a resist composition comprising a polymer and an optional acid generator onto a substrate, said polymer comprising recurring units (a1) having an acid labile group of formula (1a), represented by the general formula (1):

wherein R¹ is hydrogen or methyl, and the broken line designates a valence bond,

prebaking the composition to form a resist film,

exposing a selected region of the resist film to high-energy radiation,

baking, and

developing the exposed film in an organic solvent-based developer to form a negative pattern wherein the unexposed region of resist film is dissolved away and the exposed region of resist film is not dissolved.

In one preferred embodiment, polymer further comprises recurring units (a2) represented by the general formula (2) and recurring units of at least one type selected from recurring units (b1) to (b4) represented by the general formula (3).

Herein R¹⁰ is hydrogen or methyl, R¹¹ is an acid labile group other than formula (1a), and X¹ is a single bond, phenylene, naphthylene, or —C(═O)—O—R¹²— wherein R¹² is a straight, branched or cyclic C₁-C₁₀ alkylene group which may contain an ether radical, ester radical, lactone ring or hydroxyl radical, or a phenylene or naphthylene group, a2 is a number in the range: 0≦a2<1.0.

Herein R¹³ and R¹⁶ each are hydrogen or methyl; R¹⁴ is a di- to pentavalent, straight, branched or cyclic C₁-C₁₆ aliphatic hydrocarbon group which may contain an ether or ester radical; R¹⁵ and R¹⁷ each are an acid labile group; R¹⁸ to R²¹ and R²² to R²⁵ are each independently hydrogen, cyano, a straight, branched or cyclic C₁-C₆ alkyl group, alkoxycarbonyl, or a group having an ether radical or lactone ring, at least one of R¹⁸ to R²¹ and R²² to R²⁵ has a hydroxyl group substituted with an acid labile group; m is an integer of 1 to 4, n is 0 or 1, b1, b2, b3 and b4 are numbers in the range: 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, 0≦b1+b2+b3+b4<1.0, and 0<a2+b1+b2+b3+b4<1.0.

In another preferred embodiment, the polymer further comprises recurring units derived from a monomer having an adhesive group, but not an acid labile group, the adhesive group being selected from the group consisting of a hydroxyl, cyano, carbonyl, ester, ether, lactone ring, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone and carbonate group.

In a further preferred embodiment, the polymer further comprises recurring units of at least one type selected from recurring units (d1), (d2) and (d3) represented by the general formula.

Herein R⁰²⁰, R⁰²⁴ and R⁰²⁸ each are hydrogen or methyl, R⁰²¹ is a single bond, phenylene, —O—R⁰³³—, or —C(═O)—Y—R⁰³³—, Y is oxygen or NH, R⁰³³ is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl (—CO—), ester (—COO—), ether (—O—) or hydroxyl radical, R⁰²², R⁰²³, R⁰²⁵, R⁰²⁶, R⁰²⁷, R⁰²⁹, and R⁰³¹ are each independently a straight, branched or cyclic C₁-C₁₂ alkyl group which may contain a carbonyl, ester or ether radical, or a C₆-C₁₂ aryl, C₇-C₂₀ aralkyl, or thiophenyl group, Z¹ is a single bond, methylene, ethylene, phenylene, fluorophenylene, —O—R⁰³²—, or —C(═O)—Z²—R⁰³²—, Z² is oxygen or NH, R⁰³² is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl, ester, ether or hydroxyl radical, M is a non-nucleophilic counter ion, d1, d2 and d3 are numbers in the range: 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, and 0≦d1+d2+d3≦0.3.

In one preferred embodiment, the resist composition comprises component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2): R¹¹⁶—SO₃ ⁻M₂ ⁺  (Z1) R¹¹⁷—COO⁻M₂ ⁺  (Z2) wherein R¹¹⁶ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of sulfonic acid, R¹¹⁷ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of carboxylic acid, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.

More preferably, component Z is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z3) or (Z4):

wherein R¹¹⁸, R¹²⁰ and R¹²¹ each are hydrogen or trifluoromethyl, R¹¹⁹ is hydrogen, hydroxyl, a substituted or unsubstituted, straight, branched or cyclic C₁-C₂₀ alkyl group or a substituted or unsubstituted C₆-C₃₀ aryl group, p is an integer of 1 to 3, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.

Preferably, the developer comprises at least one organic solvent selected from among 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, methyl-acetophenone, propyl acetate, butyl acetate, isobutyl acetate, amyl acetate, isoamyl acetate, butenyl acetate, propyl formate, butyl formate, isobutyl formate, amyl formate, isoamyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, amyl lactate, isoamyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate.

Typically, the step of exposing the resist film to high-energy radiation includes KrF excimer laser lithography of wavelength 248 nm, ArF excimer laser lithography of wavelength 193 nm, EUV lithography of wavelength 13.5 nm or EB lithography.

Another embodiment is a pattern forming process comprising the steps of applying a resist composition comprising a polymer comprising recurring units (a1) having an acid labile group of formula (1a), represented by formula (1), an optional acid generator, and an organic solvent, onto a substrate, prebaking the composition to form a resist film, forming a protective film on the resist film, exposing a selected region of the resist film to high-energy radiation, baking, and applying an organic solvent-based developer to dissolve away the protective film and the unexposed region of resist film for forming a negative pattern wherein the exposed region of resist film is not dissolved.

In another aspect, the invention provides a negative pattern-forming resist composition comprising a polymer comprising recurring units (a1) having an acid labile group of formula (1a), represented by formula (1), an optional acid generator, and an organic solvent. The polymer is dissolvable in a developer selected from among 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, methylacetophenone, propyl acetate, butyl acetate, isobutyl acetate, amyl acetate, isoamyl acetate, butenyl acetate, propyl formate, butyl formate, isobutyl formate, amyl formate, isoamyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, amyl lactate, isoamyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate.

Preferably, the polymer further comprises recurring units (a2) represented by the general formula (2) and recurring units of at least one type selected from recurring units (b1) to (b4) represented by the general formula (3), as defined above.

Also preferably, the polymer further comprises recurring units derived from a monomer having an adhesive group, but not an acid labile group, the adhesive group being selected from among a hydroxyl, cyano, carbonyl, ester, ether, lactone ring, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone and carbonate group.

Also preferably, the polymer further comprises recurring units of at least one type selected from recurring units (d1), (d2) and (d3) represented by the above formula.

The resist composition may comprise component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2), as defined above. More preferably, component Z is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z3) or (Z4), as defined above.

Advantageous Effects of Invention

The resist composition comprising a polymer comprising recurring units having an acid labile group of tertiary ester type, specifically an acid labile group of cyclopentyl having a tert-butyl or tert-amyl pendant group as base resin exhibits a high dissolution contrast when processed by exposure, PEB and organic solvent development. A fine hole pattern can be formed with advantages including improved focal margin (DOF) and good dimensional control.

BRIEF DESCRIPTION OF DRAWINGS

The only FIGURE,

FIG. 1 is a cross-sectional view of a patterning process according one embodiment of the invention. FIG. 1A shows a photoresist film disposed on a substrate, FIG. 1B shows the resist film being exposed, and FIG. 1C shows the resist film being developed in an organic solvent.

DESCRIPTION OF EMBODIMENTS

The terms “a” and “an” herein do not denote a limitation of quantity, but rather denote the presence of at least one of the referenced item. “Optional” or “optionally” means that the subsequently described event or circumstances may or may not occur, and that description includes instances where the event or circumstance occurs and instances where it does not. As used herein, the notation (C_(n)-C_(m)) means a group containing from n to m carbon atoms per group. As used herein, the term “film” is used interchangeably with “coating” or “layer.”

The abbreviations and acronyms have the following meaning.

Mw: weight average molecular weight

Mn: number average molecular weight

Mw/Mn: molecular weight distribution or dispersity

GPC: gel permeation chromatography

PEB: post-exposure bake

PAG: photoacid generator

DOF: depth of focus

Briefly stated, the invention pertains to a resist composition comprising a polymer comprising recurring units having an acid labile group of tertiary ester type which is an acid labile group of cyclopentyl having a tert-butyl or tert-amyl pendant group, an optional acid generator, and an organic solvent; and a pattern forming process comprising the steps of applying the resist composition onto a substrate, prebaking to remove the unnecessary solvent and form a resist film, exposing a selected region of the resist film to high-energy radiation, PEB, and developing the exposed film in an organic solvent-based developer to form a negative pattern.

For the purpose of enhancing the dissolution rate of the unexposed region during organic solvent development, it is effective to introduce an acid labile group having alkyl group of branched structure. Solvation takes place in the branched portion, accelerating the dissolution rate. On the other hand, an acid labile group having cyclic structure is effective for suppressing acid diffusion.

When a tertiary ester type acid labile group composed of cyclopentyl with tert-butyl or tert-amyl pendant is incorporated, the solvent solubility is improved over the tertiary ester type acid labile group composed of cyclopentyl or adamantyl free of tert-butyl or tert-amyl pendant. On the other hand, the cyclic structure is effective for suppressing acid diffusion. A negative pattern featuring low diffusion and a high contrast can be formed via organic solvent development.

The tertiary ester type acid labile group is an acid labile group of cyclopentyl with tert-butyl or tert-amyl pendant, represented by the general formula (1a). The recurring unit having a carboxyl group whose hydrogen is substituted by this tertiary ester type acid labile group is represented by the general formula (1).

Herein R¹ is hydrogen or methyl, and the broken line designates a valence bond.

Examples of the recurring unit (a1) of formula (1) are shown below.

In addition to the recurring units (a1), the polymer may have copolymerized therein recurring units (a2) having an acid labile group other than formula (1) substituted thereon, as represented by the general formula (2).

Herein, R¹⁰ is hydrogen or methyl, R¹¹ is an acid labile group other than formula (1), and X¹ is a single bond, phenylene, naphthylene, or —C(═O)—O—R¹²— wherein R¹² is a straight, branched or cyclic C₁-C₁₀ alkylene group which may contain an ether radical, ester radical, lactone ring or hydroxyl radical, or a phenylene or naphthylene group, a2 is a number in the range: 0≦a2<1.0. The acid labile group R¹¹ will be described later.

In addition to the recurring units (a1) of formula (1) and recurring units (a2) of formula (2), the polymer may have further copolymerized therein recurring units having a hydroxyl group substituted with an acid labile group. Suitable recurring units having an acid labile group-substituted hydroxyl group include those units having the general formulae (b1) to (b4).

Herein R¹³ and R¹⁶ are each independently hydrogen or methyl. R¹⁴ is a di- to pentavalent, straight, branched or cyclic C₁-C₁₆ aliphatic hydrocarbon group which may contain an ether or ester radical. R¹⁵ and R¹⁷ each are an acid labile group. R¹⁸ to R²¹ and R²² to R²⁵ are each independently hydrogen, cyano, a straight, branched or cyclic C₁-C₆ alkyl group, alkoxycarbonyl, or a group having an ether radical or lactone ring, at least one of R¹⁸ to R²¹ and R²² to R²⁵ has a hydroxyl group substituted with an acid labile group. The subscript m is an integer of 1 to 4, and n is 0 or 1, b1, b2, b3 and b4 are numbers in the range: 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, and 0≦b1+b2+b3+b4<1.0.

Examples of the monomers from which recurring units (b1) and (b2) are derived are shown below wherein R¹³ and R¹⁶ each are hydrogen or methyl, R¹⁵ and R¹⁷ each are an acid labile group.

Examples of the monomers from which recurring units (b3) and (b4) are derived are shown below wherein R is an acid labile group.

The acid labile group R¹¹ (other than formula (1)) substituting on the carboxyl group in formula (2) and the acid labile groups R¹⁵, R¹⁷, any one of R¹⁸ to R²¹, and any one of R²² to R²⁵ substituting on the hydroxyl group in formula (3) may be selected from a variety of such groups while they may be the same or different. Suitable acid labile groups include groups of the formula (AL-10), acetal groups of the formula (AL-11), tertiary alkyl groups of the formula (AL-12), and C₄-C₂₀ oxoalkyl groups, but are not limited thereto.

In formulae (AL-10) and (AL-11), R⁵¹ and R⁵⁴ each are a monovalent hydrocarbon group, typically straight, branched or cyclic alkyl group, of 1 to 40 carbon atoms, more specifically 1 to 20 carbon atoms, which may contain a heteroatom such as oxygen, sulfur, nitrogen or fluorine. R⁵² and R⁵³ each are hydrogen or a monovalent hydrocarbon group, typically straight, branched or cyclic alkyl group, of 1 to 20 carbon atoms which may contain a heteroatom such as oxygen, sulfur, nitrogen or fluorine. The subscript “a5” is an integer of 0 to 10, and especially 1 to 5. Alternatively, a pair of R⁵² and R⁵³, R⁵² and R⁵⁴, or R⁵³ and R⁵⁴ may bond together to form a ring, specifically aliphatic ring, with the carbon atom or the carbon and oxygen atoms to which they are attached, the ring having 3 to 20 carbon atoms, especially 4 to 16 carbon atoms.

In formula (AL-12), R⁵⁵, R⁵⁶ and R⁵⁷ each are a monovalent hydrocarbon group, typically straight, branched or cyclic alkyl group, of 1 to 20 carbon atoms which may contain a heteroatom such as oxygen, sulfur, nitrogen or fluorine. Alternatively, a pair of R⁵⁵ and R⁵⁶, R⁵⁵ and R⁵⁷, or R⁵⁶ and R⁵⁷ may bond together to form a ring, specifically aliphatic ring, with the carbon atom to which they are attached, the ring having 3 to 20 carbon atoms, especially 4 to 16 carbon atoms.

Illustrative examples of the acid labile group of formula (AL-10) include tert-butoxycarbonyl, tert-butoxycarbonylmethyl, tert-amyloxycarbonyl, tert-amyloxycarbonylmethyl, 1-ethoxyethoxycarbonylmethyl, 2-tetrahydropyranyloxycarbonylmethyl and 2-tetrahydrofuranyloxycarbonylmethyl as well as substituent groups of the following formulae (AL-10)-1 to (AL-10)-10.

In formulae (AL-10)-1 to (AL-10)-10, R⁵⁸ is each independently a straight, branched or cyclic C₁-C₈ alkyl group, C₆-C₂₀ aryl group or C₇-C₂₀ aralkyl group; R⁵⁹ is hydrogen or a straight, branched or cyclic C₁-C₂₀ alkyl group; R⁶⁰ is a C₆-C₂₀ aryl group or C₇-C₂₀ aralkyl group; and a5 is an integer of 0 to 10, especially 1 to 5. It is excluded from formula (AL-10)-1 that R⁵⁸ is tert-butyl or tert-amyl.

Illustrative examples of the acetal group of formula (AL-11) include those of the following formulae (AL-11)-1 to (AL-11)-112.

Other examples of acid labile groups include those of the following formula (AL-11a) or (AL-11b) while the polymer may be crosslinked within the molecule or between molecules with these acid labile groups.

Herein R⁶¹ and R⁶² each are hydrogen or a straight, branched or cyclic C₁-C₈ alkyl group, or R⁶¹ and R⁶² may bond together to form a ring with the carbon atom to which they are attached, and R⁶¹ and R⁶² stand for a straight or branched C₁-C₈ alkylene group when they form a ring. R⁶³ is a straight, branched or cyclic C₁-C₁₀ alkylene group. Each of b5 and d5 is 0 or an integer of 1 to 10, preferably 0 or an integer of 1 to 5, and c5 is an integer of 1 to 7. “A” is a (c5+1)-valent aliphatic or alicyclic saturated hydrocarbon group, aromatic hydrocarbon group or heterocyclic group having 1 to 50 carbon atoms, which may be separated by a heteroatom such as oxygen, sulfur or nitrogen or in which some hydrogen atoms attached to carbon atoms may be substituted by hydroxyl, carboxyl, carbonyl radicals or fluorine atoms. “B” is —CO—O—, —NHCO—O— or —NHCONH—.

Preferably, “A” is selected from divalent to tetravalent, straight, branched or cyclic C₁-C₂₀ alkylene, alkanetriyl and alkanetetrayl groups, and C₆-C₃₀ arylene groups, which may be separated by a heteroatom such as oxygen, sulfur or nitrogen or in which some hydrogen atoms attached to carbon atoms may be substituted by hydroxyl, carboxyl, acyl radicals or halogen atoms. The subscript c5 is preferably an integer of 1 to 3.

The crosslinking acetal groups of formulae (AL-11a) and (AL-11b) are exemplified by the following formulae (AL-11)-113 through (AL-11)-120.

Illustrative examples of the tertiary alkyl group of formula (AL-12) include tert-butyl, triethylcarbyl, 1-ethylnorbornyl, 1-methylcyclohexyl, 1-ethylcyclopentyl, and tert-amyl groups as well as those of (AL-12)-1 to (AL-12)-16.

Herein R⁶⁴ is each independently a straight, branched or cyclic C₁-C₈ alkyl group, C₆-C₂₀ aryl group or C₇-C₂₀ aralkyl group, or two R⁶⁴ groups may bond together to form a ring. R⁶⁵ and R⁶⁷ each are hydrogen, methyl or ethyl. R⁶⁶ is a C₆-C₂₀ aryl group or C₇-C₂₀ aralkyl group.

With acid labile groups containing R⁶⁸ representative of a di- or poly-valent alkylene or arylene group as shown by formula (AL-12)-17, the polymer may be crosslinked within the molecule or between molecules. In formula (AL-12)-17, R⁶⁴ is as defined above, R⁶⁸ is a single bond, a straight, branched or cyclic C₁-C₂₀ alkylene group or arylene group, which may contain a heteroatom such as oxygen, sulfur or nitrogen, and b6 is an integer of 0 to 3. It is noted that formula (AL-12)-17 is applicable to all the foregoing acid labile groups.

The groups represented by R⁶⁴, R⁶⁵, R⁶⁶ and R⁶⁷ may contain a heteroatom such as oxygen, nitrogen or sulfur. Such groups are exemplified by those of the following formulae (AL-13)-1 to (AL-13)-7.

While the polymer used as the base resin in the resist composition comprises essentially recurring units (a1) of formula (1), and optionally (and preferably) recurring units (a2) of formula (2), acid labile group-containing recurring units (b1) to (b4) of formula (3), it may have further copolymerized therein recurring units (c) derived from a monomer having an adhesive group, but not an acid labile group. Suitable adhesive groups include hydroxyl, cyano, carbonyl, ester, ether groups, lactone rings, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone, and carbonate groups. Of these, recurring units having lactone ring as the adhesive group are most preferred.

Examples of suitable monomers from which recurring units (c) are derived are given below.

In a preferred embodiment, the polymer has further copolymerized therein units selected from sulfonium salts (d1) to (d3) represented by the general formulae below.

Herein R⁰²⁰, R⁰²⁴ and R⁰²⁸ each are hydrogen or methyl. R⁰²¹ is a single bond, phenylene, —O—R⁰³³—, or —C(═O)—Y—R⁰³³— wherein Y is oxygen or NH, and R⁰³³ is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl (—CO—), ester (—COO—), ether (—O—) or hydroxyl radical. R⁰²², R⁰²³, R⁰²⁵, R⁰²⁶, R⁰²⁷, R⁰²⁹, R⁰³⁰, and R⁰³¹ are each independently a straight, branched or cyclic C₁-C₁₂ alkyl group which may contain a carbonyl, ester or ether radical, or a C₆-C₁₂ aryl, C₇-C₂₀ aralkyl, or thiophenyl group. Z¹ is a single bond, methylene, ethylene, phenylene, fluorophenylene, —O—R⁰³²—, or —C(═O)—Z²—R⁰³²— where in Z is oxygen or NH, and R⁰³² is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl, ester, ether or hydroxyl radical. M⁻ is a non-nucleophilic counter ion, d1, d2 and d3 are numbers in the range: 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, and 0≦d1+d2+d3≦0.3.

Besides the recurring units described above, the polymer may have further copolymerized therein additional recurring units, for example, recurring units (e) having a non-leaving hydrocarbon group as described in JP-A 2008-281980. Examples of the non-leaving hydrocarbon group other than those described in JP-A 2008-281980 include indene, acenaphthylene, and norbornadiene derivatives. Copolymerization of recurring units (e) having a non-leaving hydrocarbon group is effective for improving the dissolution of the polymer in organic solvent-based developer.

It is also possible to incorporate recurring units (f) having an oxirane or oxetane ring into the polymer. Where recurring units (f) having an oxirane or oxetane ring are copolymerized in the polymer, the exposed region of resist film will be crosslinked, leading to improvements in film retention of the exposed region and etch resistance. Examples of the recurring units (f) having an oxirane or oxetane ring are given below wherein R⁴¹ is hydrogen or methyl.

Appropriate molar fractions of individual recurring units (a1), (a2), (b1), (b2), (b3), (b4), (c), (d1), (d2), (d3), (e) and (f) are in the range: 0<a1<1.0, 0≦a2<1.0, 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, 0≦a2+b1+b2+b3+b4<1.0, 0<c<1.0, 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, 0≦d1+d2+d3≦0.3, 0≦e≦0.4, and 0≦f≦0.6;

more preferably 0.1≦a1≦0.9, 0≦a2≦0.9, 0.1≦a1+a2≦0.9, 0≦b1≦0.9, 0≦b2≦0.9, 0≦b3≦0.9, 0≦b4≦0.9, 0.1≦a1+a2+b1+b2+b3+b4≦0.9, 0.1≦c≦0.9, 0≦d1≦0.2, 0≦d2≦0.2, 0≦d3≦0.2, 0≦d1+d2+d3≦0.2, 0≦e≦0.3, and 0≦f≦0.5,

provided that a1+a2+b1+b2+b3+b4+c+d1+d2+d3+e+f=1.

The polymer serving as the base resin in the resist composition used in the pattern forming process of the invention should preferably have a weight average molecular weight (Mw) in the range of 1,000 to 500,000, and more preferably 2,000 to 15,000, as measured by GPC versus polystyrene standards using tetrahydrofuran solvent. With too low a Mw, a film thickness loss is likely to occur upon organic solvent development. A polymer with too high a Mw may lose solubility in organic solvent and have a likelihood of footing after pattern formation.

If a polymer has a wide molecular weight distribution or dispersity (Mw/Mn), which indicates the presence of lower and higher molecular weight polymer fractions, there is a possibility that following exposure, foreign matter is left on the pattern or the pattern profile is exacerbated. The influences of molecular weight and dispersity become stronger as the pattern rule becomes finer. Therefore, the multi-component copolymer should preferably have a narrow dispersity (Mw/Mn) of 1.0 to 2.0, especially 1.0 to 1.5, in order to provide a resist composition suitable for micropatterning to a small feature size.

The polymer used herein may be synthesized by any desired method, for example, by dissolving unsaturated bond-containing monomers corresponding to the respective units (a1), (a2), (b1), (b2), (b3), (b4), (c), (d1), (d2), (d3), (e), and (f) in an organic solvent, adding a radical initiator thereto, and effecting heat polymerization. Examples of the organic solvent which can be used for polymerization include toluene, benzene, tetrahydrofuran, diethyl ether and dioxane. Examples of the polymerization initiator used herein include 2,2′-azobisisobutyronitrile (AIBN), 2,2′-azobis(2,4-dimethylvaleronitrile), dimethyl 2,2-azobis(2-methylpropionate), benzoyl peroxide, and lauroyl peroxide. Preferably the system is heated at 50 to 100° C. for polymerization to take place. The reaction time is preferably 4 to 24 hours. The acid labile group that has been incorporated in the monomers may be kept as such, or the product may be protected or partially protected after polymerization.

It is acceptable to use a blend of two or more polymers which differ in compositional ratio, molecular weight or dispersity as well as a blend of an inventive polymer and another polymer free of an acid labile group-substituted carboxyl group as represented by formula (1) or a blend of an inventive polymer and a polymer comprising recurring units having a conventional acid labile group-substituted hydroxyl or carboxyl group, for example, a polymer comprising recurring units (a2) and/or (b1) to (b4).

In a further embodiment, the inventive polymer may be blended with a polymer of the conventional type wherein the exposed region is dissolved on alkaline development such as (meth)acrylate polymer, polynorbornene, cycloolefin-maleic anhydride copolymer, or ring-opening metathesis polymerization (ROMP) polymer. Also, the inventive polymer may be blended with a (meth)acrylate polymer, polynorbornene, or cycloolefin-maleic anhydride copolymer having an acid labile group-substituted hydroxyl group wherein the exposed region is not dissolved by alkaline development, but a negative pattern is formed by organic solvent development.

Resist Composition

The resist composition used in the pattern forming process of the invention may further comprise an organic solvent, and optionally, a compound capable of generating an acid in response to high-energy radiation (known as “acid generator”), dissolution regulator, basic compound, surfactant, acetylene alcohol, and other components.

The resist composition used herein may include an acid generator in order for the composition to function as a chemically amplified resist composition. Typical of the acid generator used herein is a photoacid generator (PAG) capable of generating an acid in response to actinic light or radiation. The PAG may preferably be compounded in an amount of 0.5 to 30 parts and more preferably 1 to 20 parts by weight per 100 parts by weight of the base resin. The PAG is any compound capable of generating an acid upon exposure to high-energy radiation. Suitable PAGs include sulfonium salts, iodonium salts, sulfonyldiazomethane, N-sulfonyloxyimide, and oxime-O-sulfonate acid generators. The PAGs may be used alone or in admixture of two or more. Typically acid generators generate such acids as sulfonic acids, imidic acids and methide acids. Of these, sulfonic acids which are fluorinated at α-position are most commonly used. In case the acid labile group is an acetal group which is susceptible to deprotection, the sulfonic acid need not necessarily be fluorinated at α-position. In the embodiment wherein the base polymer has recurring units (d1), (d2) or (d3) of acid generator copolymerized therein, the acid generator need not be separately added.

In a preferred embodiment, the resist composition comprises component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2). R¹¹⁶—SO₃ ⁻M₂ ⁺  (Z1) R¹¹⁷—COO⁻M₂ ⁺  (Z2) Herein R¹¹⁶ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at α-position of sulfonic acid. R¹¹⁷ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at α-position of carboxylic acid. M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.

More preferably, component Z is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z3) or (Z4).

Herein R¹¹⁸, R¹²⁰ and R¹²¹ each are hydrogen or trifluoromethyl. R¹¹⁹ is hydrogen, hydroxyl, a substituted or unsubstituted, straight, branched or cyclic C₁-C₂₀ alkyl group or a substituted or unsubstituted C₆-C₃₀ aryl group, p is an integer of 1 to 3, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.

Inclusion of an onium salt having formula (Z3) or (Z4) as component Z enables to form a hole pattern with the advantages of further improved focal margin (DOF) and dimensional control. Preferably component Z is used in an amount of 0.5 to 15 parts by weight per 100 parts by weight of the base resin. Within this range, the benefits of the invention are more effectively achievable.

Illustrative examples of component Z are given below, but not limited thereto.

To the resist composition, a basic compound may be added. The preferred basic compound is a compound capable of holding down the diffusion rate of acid when the acid generated by the acid generator diffuses in the resist film. The inclusion of the basic compound holds down the diffusion rate of acid in the resist film, which leads to many advantages including improved resolution, minimized sensitivity change following exposure, reduced substrate poisoning and environment dependency, and improved exposure latitude and pattern profile.

Exemplary basic compounds include primary, secondary and tertiary amine compounds, specifically amine compounds having a hydroxyl, ether, ester, lactone, cyano or sulfonic acid ester group, as described in JP-A 2008-111103 (U.S. Pat. No. 7,537,880), paragraphs [0146] to [0164], and compounds having a carbamate group, as described in JP-A 2001-166476. The basic compound is preferably used in an amount of 0 to 5 parts, more preferably 0.1 to 5 parts by weight per 100 parts by weight of the base resin.

Examples of the organic solvent used herein are described in JP-A 2008-111103, paragraphs [0144] to [0145]. Specifically, exemplary solvents include ketones such as cyclohexanone and methyl-2-n-amyl ketone; alcohols such as 3-methoxybutanol, 3-methyl-3-methoxybutanol, 1-methoxy-2-propanol, and 1-ethoxy-2-propanol; ethers such as propylene glycol monomethyl ether, ethylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monoethyl ether, propylene glycol dimethyl ether, and diethylene glycol dimethyl ether; esters such as propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monoethyl ether acetate, ethyl lactate, ethyl pyruvate, butyl acetate, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, tert-butyl acetate, tert-butyl propionate, and propylene glycol mono-tert-butyl ether acetate; and lactones such as γ-butyrolactone, and mixtures thereof. Where the acid labile group used is of acetal type, a high-boiling alcohol solvent may be added for accelerating deprotection reaction of acetal, for example, diethylene glycol, propylene glycol, glycerol, 1,4-butane diol, and 1,3-butane diol.

The organic solvent is preferably used in an amount of 100 to 10,000 parts, more preferably 300 to 8,000 parts by weight per 100 parts by weight of the base resin.

Exemplary surfactants are described in JP-A 2008-111103, paragraphs [0165] to [0166]. Exemplary dissolution regulators are described in JP-A 2008-122932 (US 2008090172), paragraphs [0155] to [0178], and exemplary acetylene alcohols in paragraphs [0179] to [0182].

Also a polymeric additive may be added for improving the water repellency on surface of a resist film as spin coated. This additive may be used in the topcoatless immersion lithography. The additive has a specific structure with a 1,1,1,3,3,3-hexafluoro-2-propanol residue and is described in JP-A 2007-297590 and JP-A 2008-111103. The water repellency improver to be added to the resist composition should be soluble in the organic solvent as the developer. The water repellency improver of specific structure with a 1,1,1,3,3,3-hexafluoro-2-propanol residue is well soluble in the developer. A polymer having an amino group or amine salt copolymerized as recurring units may serve as the water repellent additive and is effective for preventing evaporation of acid during PEB and avoiding any hole pattern opening failure after development. An appropriate amount of the water repellency improver is 0.1 to 20 parts, preferably 0.5 to 10 parts by weight per 100 parts by weight of the base resin.

Notably, the amounts of the dissolution regulator, surfactant and acetylene alcohol added may be determined as appropriate for their purpose of addition.

Process

The pattern forming process of the invention comprises the steps of coating a resist composition onto a substrate, prebaking the resist composition to form a resist film, exposing a selected region of the resist film to high-energy radiation, PEB, and developing the exposed resist film in an organic solvent developer so that the unexposed region of resist film is dissolved and the exposed region of resist film is left, thereby forming a negative tone resist pattern such as a hole or trench pattern.

FIG. 1 illustrates the pattern forming process of the invention. First, the resist composition is coated on a substrate to form a resist film thereon. Specifically, a resist film 40 of a resist composition is formed on a processable substrate 20 disposed on a substrate 10 directly or via an intermediate intervening layer 30 as shown in FIG. 1A. The resist film preferably has a thickness of 10 to 1,000 nm and more preferably 20 to 500 nm. Prior to exposure, the resist film is heated or prebaked, preferably at a temperature of 60 to 180° C., especially 70 to 150° C. for a time of 10 to 300 seconds, especially 15 to 200 seconds.

The substrate 10 used herein is generally a silicon substrate. The processable substrate (or target film) 20 used herein includes SiO₂, SiN, SiON, SiOC, p-Si, α-Si, TiN, WSi, BPSG, SOG, Cr, CrO, CrON, MoSi, low dielectric film, and etch stopper film. The intermediate intervening layer 30 includes hard masks of SiO₂, SiN, SiON or p-Si, an undercoat in the form of carbon film, a silicon-containing intermediate film, and an organic antireflective coating.

Next comes exposure depicted at 50 in FIG. 1B. For the exposure, preference is given to high-energy radiation having a wavelength of 140 to 250 nm, EUV having a wavelength of 13.5 nm, and EB, and especially ArF excimer laser radiation of 193 nm. The exposure may be done either in a dry atmosphere such as air or nitrogen stream or by immersion lithography in water. The ArF immersion lithography uses deionized water or liquids having a refractive index of at least 1 and highly transparent to the exposure wavelength such as alkanes as the immersion solvent. In the immersion lithography, the resist film as prebaked is exposed to light through a projection lens while water is introduced between the resist film and the projection lens. Since this allows lenses to be designed to a NA of 1.0 or higher, formation of finer feature size patterns is possible. The immersion lithography is important for the ArF lithography to survive to the 45-nm node. In the case of immersion lithography, deionized water rinsing (or post-soaking) may be carried out after exposure for removing water droplets left on the resist film, or a protective film may be applied onto the resist film after pre-baking for preventing any leach-out from the resist film and improving water slip on the film surface.

The resist protective film used in the immersion lithography is preferably formed from a solution of a polymer having 1,1,1,3,3,3-hexafluoro-2-propanol residues which is insoluble in water, but soluble in an alkaline developer liquid, in a solvent selected from alcohols of at least 4 carbon atoms, ethers of 8 to 12 carbon atoms, and mixtures thereof. The protective film-forming composition used herein may be based on a polymer comprising recurring units derived from a monomer having a 1,1,1,3,3,3-hexafluoro-2-propanol residue. While the protective film must dissolve in the organic solvent developer, the polymer comprising recurring units derived from a monomer having a 1,1,1,3,3,3-hexafluoro-2-propanol residue dissolves in organic solvent developers. In particular, protective film-forming materials having 1,1,1,3,3,3-hexafluoro-2-propanol residues as described in JP-A 2007-025634 and JP-A 2008-003569 readily dissolve in organic solvent developers.

In the protective film-forming composition, an amine compound or amine salt or a polymer having copolymerized therein recurring units containing an amine compound or amine salt may be used. This component is effective for controlling diffusion of the acid generated in the exposed region of the photoresist film to the unexposed region for thereby preventing any hole opening failure. Useful protective film materials having an amine compound added thereto are described in JP-A 2008-003569, and useful protective film materials having an amino group or amine salt copolymerized are described in JP-A 2007-316448. The amine compound or amine salt may be selected from the compounds enumerated as the basic compound to be added to the resist composition. An appropriate amount of the amine compound or amine salt added is 0.01 to 10 parts, preferably 0.02 to 8 parts by weight per 100 parts by weight of the base resin.

After formation of the photoresist film, deionized water rinsing (or post-soaking) may be carried out for extracting the acid generator and the like from the film surface or washing away particles, or after exposure, rinsing (or post-soaking) may be carried out for removing water droplets left on the resist film. If the acid evaporating from the exposed region during PEB deposits on the unexposed region to deprotect the protective group on the surface of the unexposed region, there is a possibility that the surface edges of holes after development are bridged to close the holes. Particularly in the case of negative development, regions surrounding the holes receive light so that acid is generated therein. There is a possibility that the holes are not opened if the acid outside the holes evaporates and deposits inside the holes during PEB. Provision of a protective film is effective for preventing evaporation of acid and for avoiding any hole opening failure. A protective film having an amine compound added thereto is more effective for preventing acid evaporation. On the other hand, a protective film to which an acid compound such as a carboxyl or sulfo group is added or which is based on a polymer having copolymerized therein monomeric units containing a carboxyl or sulfo group is undesirable because of a potential hole opening failure.

The other embodiment of the invention is a process for forming a pattern by applying a resist composition comprising a polymer comprising recurring units having formula (1), an optional acid generator, and an organic solvent onto a substrate, baking the composition to form a resist film, forming a protective film on the resist film, exposing the resist film to high-energy radiation to define exposed and unexposed regions, PEB, and applying an organic solvent-based developer to the coated substrate to form a negative pattern wherein the unexposed region of resist film and the protective film are dissolved and the exposed region of resist film is not dissolved. The protective film is preferably formed from a composition comprising a polymer bearing a 1,1,1,3,3,3-hexafluoro-2-propanol residue and an amino group or amine salt-containing compound, or a composition comprising a polymer bearing a 1,1,1,3,3,3-hexafluoro-2-propanol residue and having amino group or amine salt-containing recurring units copolymerized, the composition further comprising an alcohol solvent of at least 4 carbon atoms, an ether solvent of 8 to 12 carbon atoms, or a mixture thereof.

Examples of suitable recurring units having a 1,1,1,3,3,3-hexafluoro-2-propanol residue include those derived from hydroxyl-bearing monomers selected from among the monomers listed for units (c) on pages 49, 50 and 51. Examples of the amino group-containing compound include the amine compounds described in JP-A 2008-111103, paragraphs [0146] to [0164] as being added to photoresist compositions. Examples of the amine salt-containing compound include salts of the foregoing amine compounds with carboxylic acids or sulfonic acids.

Suitable alcohols of at least 4 carbon atoms include 1-butyl alcohol, 2-butyl alcohol, isobutyl alcohol, tert-butyl alcohol, 1-pentanol, 2-pentanol, 3-pentanol, tert-amyl alcohol, neopentyl alcohol, 2-methyl-1-butanol, 3-methyl-1-butanol, 3-methyl-3-pentanol, cyclopentanol, 1-hexanol, 2-hexanol, 3-hexanol, 2,3-dimethyl-2-butanol, 3,3-dimethyl-1-butanol, 3,3-dimethyl-2-butanol, 2-ethyl-1-butanol, 2-methyl-1-pentanol, 2-methyl-2-pentanol, 2-methyl-3-pentanol, 3-methyl-1-pentanol, 3-methyl-2-pentanol, 3-methyl-3-pentanol, 4-methyl-1-pentanol, 4-methyl-2-pentanol, 4-methyl-3-pentanol, cyclohexanol, and 1-octanol. Suitable ether solvents of 8 to 12 carbon atoms include di-n-butyl ether, diisobutyl ether, di-sec-butyl ether, di-n-pentyl ether, diisopentyl ether, di-sec-pentyl ether, di-tert-amyl ether, and di-n-hexyl ether.

Exposure is preferably performed in an exposure dose of about 1 to 200 mJ/cm², more preferably about 10 to 100 mJ/cm². This is followed by baking (PEB) on a hot plate at 60 to 150° C. for 1 to 5 minutes, preferably at 80 to 120° C. for 1 to 3 minutes.

Thereafter the exposed resist film is developed in a developer consisting of an organic solvent for 0.1 to 3 minutes, preferably 0.5 to 2 minutes by any conventional techniques such as dip, puddle and spray techniques. In this way, the unexposed region of resist film was dissolved away, leaving a negative resist pattern 40 on the substrate 10 as shown in FIG. 1C. The developer used herein is preferably selected from among ketones such as 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, and methylacetophenone, and esters such as propyl acetate, butyl acetate, isobutyl acetate, amyl acetate, butenyl acetate, isoamyl acetate, propyl formate, butyl formate, isobutyl formate, amyl formate, isoamyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, amyl lactate, isoamyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate, and mixtures thereof. One or more of these solvents may be used as the developer. When a mixture of plural solvents is used, they may be mixed in any desired ratio. A surfactant may be added to the developer while it may be selected from the same list of compounds as exemplified for the surfactant to be added to the resist composition.

At the end of development, the resist film is rinsed. As the rinsing liquid, a solvent which is miscible with the developer and does not dissolve the resist film is preferred. Suitable solvents include alcohols of 3 to 10 carbon atoms, ether compounds of 8 to 12 carbon atoms, alkanes, alkenes, and alkynes of 6 to 12 carbon atoms, and aromatic solvents. Specifically, suitable alkanes of 6 to 12 carbon atoms include hexane, heptane, octane, nonane, decane, undecane, dodecane, methylcyclopentane, dimethylcyclopentane, cyclohexane, methylcyclohexane, dimethylcyclohexane, cycloheptane, cyclooctane, and cyclononane. Suitable alkenes of 6 to 12 carbon atoms include hexene, heptene, octene, cyclohexene, methylcyclohexene, dimethylcyclohexene, cycloheptene, and cyclooctene. Suitable alkynes of 6 to 12 carbon atoms include hexyne, heptyne, and octyne. Suitable alcohols of 3 to 10 carbon atoms include n-propyl alcohol, isopropyl alcohol, 1-butyl alcohol, 2-butyl alcohol, isobutyl alcohol, tert-butyl alcohol, 1-pentanol, 2-pentanol, 3-pentanol, tert-amyl alcohol, neopentyl alcohol, 2-methyl-1-butanol, 3-methyl-1-butanol, 3-methyl-3-pentanol, cyclopentanol, 1-hexanol, 2-hexanol, 3-hexanol, 2,3-dimethyl-2-butanol, 3,3-dimethyl-1-butanol, 3,3-dimethyl-2-butanol, 2-ethyl-1-butanol, 2-methyl-1-pentanol, 2-methyl-2-pentanol, 2-methyl-3-pentanol, 3-methyl-1-pentanol, 3-methyl-2-pentanol, 3-methyl-3-pentanol, 4-methyl-1-pentanol, 4-methyl-2-pentanol, 4-methyl-3-pentanol, cyclohexanol, and 1-octanol. Suitable ether compounds of 8 to 12 carbon atoms include di-n-butyl ether, diisobutyl ether, di-sec-butyl ether, di-n-pentyl ether, diisopentyl ether, di-sec-pentyl ether, di-tert-amyl ether, and di-n-hexyl ether. The solvents may be used alone or in admixture. Besides the foregoing solvents, aromatic solvents may be used, for example, toluene, xylene, ethylbenzene, isopropylbenzene, tert-butylbenzene and mesitylene. Rinsing is effective for minimizing the risks of resist pattern collapse and defect formation.

However, rinsing is not essential. If rinsing is omitted, the amount of solvent used may be reduced.

A hole pattern after reversal may be shrunk by the RELACS® process. A hole pattern is shrunk by coating a shrink agent thereto, and baking such that the shrink agent may undergo crosslinking at the resist surface as a result of the acid catalyst diffusing from the resist layer during bake, and the shrink agent may attach to the sidewall of the hole pattern. The bake is at a temperature of 70 to 180° C., preferably 80 to 170° C., for a time of 10 to 300 seconds. The extra shrink agent is stripped and the hole pattern is shrunk.

Where a hole pattern is formed by negative tone development, exposure by double dipole illuminations of X- and Y-direction line patterns provides the highest contrast light. The contrast may be further increased by combining dipole illumination with s-polarized illumination.

When a halftone phase shift mask bearing a lattice-like shifter pattern is used, a pattern of holes may be formed at the intersections between gratings of the lattice-like shifter pattern after development, as described in JP-A 2011-170316, paragraph [0097] (US 20110177462). The preferred halftone phase shift mask bearing a lattice-like shifter pattern has a transmittance of 3 to 15%. More preferably, the phase shift mask used is a phase shift mask including a lattice-like first shifter having a line width equal to or less than a half pitch and a second shifter arrayed on the first shifter and consisting of lines whose on-wafer size is 2 to 30 nm thicker than the line width of the first shifter, whereby a pattern of holes is formed only where the thick shifter is arrayed. Also preferably, the phase shift mask used is a phase shift mask including a lattice-like first shifter having a line width equal to or less than a half pitch and a second shifter arrayed on the first shifter and consisting of dots whose on-wafer size is 2 to 100 nm thicker than the line width of the first shifter, whereby a pattern of holes is formed only where the thick shifter is arrayed.

Exposure by double dipole illuminations of X- and Y-direction lines combined with polarized illumination presents a method of forming light of the highest contrast. This method, however, has the drawback that the throughput is substantially reduced by double exposures and mask exchange therebetween. To continuously carry out two exposures while exchanging a mask, the exposure tool must be equipped with two mask stages although the existing exposure tool includes a single mask stage. Higher throughputs may be obtained by carrying out exposure of X direction lines continuously on 25 wafers in a front-opening unified pod (FOUP), exchanging the mask, and carrying out exposure continuously on the same 25 wafers, rather than exchanging a mask on every exposure of a single wafer. However, a problem arises that as the time duration until the first one of 25 wafers is exposed in the second exposure is prolonged, the environment affects the resist such that the resist after development may change its size and shape. To block the environmental impact on wafers in standby until the second exposure, it is effective that the resist film is overlaid with a protective film.

To proceed with a single mask, it is proposed in Non-Patent Document 1 to carry out two exposures by dipole illuminations in X and Y directions using a mask bearing a lattice-like pattern. When this method is compared with the above method using two masks, the optical contrast is somewhat reduced, but the throughput is improved by the use of a single mask. As described in Non-Patent Document 1, the method involves forming X-direction lines in a first photoresist film by X-direction dipole illumination using a mask bearing a lattice-like pattern, insolubilizing the X-direction lines by light irradiation, coating a second photoresist film thereon, and forming Y-direction lines by Y-direction dipole illumination, thereby forming holes at the interstices between X- and Y-direction lines. Although only a single mask is needed, this method includes additional steps of insolubilizing the first photoresist pattern between the two exposures, and coating and developing the second photoresist film. Then the wafer must be removed from the exposure stage between the two exposures, giving rise to the problem of an increased alignment error. To minimize the alignment error between two exposures, two exposures must be continuously carried out without removing the wafer from the exposure stage. The addition of s-polarized illumination to dipole illumination provides a further improved contrast and is thus preferably employed. After two exposures for forming X- and Y-direction lines using a lattice-like mask are performed in an overlapping manner, negative tone development is performed whereupon a hole pattern is formed.

When it is desired to form a hole pattern via a single exposure using a lattice-like mask, a quadru-pole illumination or cross-pole illumination is used. The contrast may be improved by combining it with X-Y polarized illumination or azimuthally polarized illumination of circular polarization.

In the hole pattern forming process using the resist composition of the invention, when two exposures are involved, these exposures are carried out by changing the illumination and mask for the second exposure from those for the first exposure, whereby a fine size pattern can be formed at the highest contrast and to dimensional uniformity. The masks used in the first and second exposures bear first and second patterns of intersecting lines whereby a pattern of holes at intersections of lines is formed in the resist film after development. The first and second lines are preferably at right angles although an angle of intersection other than 90° may be employed. The first and second lines may have the same or different size and/or pitch. If a single mask bearing first lines in one area and second lines in a different area is used, it is possible to perform first and second exposures continuously. In this case, however, the maximum area available for exposure is one half. Notably, the continuous exposures lead to a minimized alignment error. Of course, the single exposure provides a smaller alignment error than the two continuous exposures.

When two exposures are performed using a single mask without reducing the exposure area, the mask pattern may be a lattice-like pattern, a dot pattern, or a combination of a dot pattern and a lattice-like pattern. The use of a lattice-like pattern contributes to the most improved light contrast, but has the drawback of a reduced resist sensitivity due to a lowering of light intensity. On the other hand, the use of a dot pattern suffers a lowering of light contrast, but provides the merit of an improved resist sensitivity.

Where holes are arrayed in horizontal and vertical directions, the above-described illumination and mask pattern are used. Where holes are arrayed at a different angle, for example, at an angle of 45°, a mask of a 45° arrayed pattern is combined with dipole illumination or cross-pole illumination.

Where two exposures are performed, a first exposure by a combination of dipole illumination with polarized illumination for enhancing the contrast of X-direction lines is followed by a second exposure by a combination of dipole illumination with polarized illumination for enhancing the contrast of Y-direction lines. Two continuous exposures with the X- and Y-direction contrasts emphasized through a single mask can be performed on a currently commercially available scanner.

The method of combining X and Y polarized illuminations with cross-pole illumination using a mask bearing a lattice-like pattern can form a hole pattern through a single exposure, despite a slight lowering of light contrast as compared with two exposures of dipole illumination. The method is estimated to attain a substantial improvement in throughput and avoids the problem of misalignment between two exposures. Using such a mask and illumination, a hole pattern of the order of 40 nm can be formed at a practically acceptable cost.

On use of a mask bearing a lattice-like pattern, light is fully shielded at intersections between gratings. A fine hole pattern may be formed by performing exposure through a mask bearing such a pattern and organic solvent development entailing positive/negative reversal.

On use of a mask bearing a dot pattern, although the contrast of an optical image is low as compared with the lattice-like pattern mask, the formation of a hole pattern is possible owing to the presence of black or light shielded spots.

It is difficult to form a fine hole pattern that holes are randomly arrayed at varying pitch and position. The super-resolution technology using off-axis illumination (such as dipole or cross-pole illumination) in combination with a phase shift mask and polarization is successful in improving the contrast of dense (or grouped) patterns, but not so the contrast of isolated patterns.

When the super-resolution technology is applied to repeating dense patterns, the pattern density bias between dense and isolated patterns, known as proximity bias, becomes a problem. As the super-resolution technology used becomes stronger, the resolution of a dense pattern is more improved, but the resolution of an isolated pattern remains unchanged. Then the proximity bias is exaggerated. In particular, an increase of proximity bias in a hole pattern resulting from further miniaturization poses a serious problem. One common approach taken to suppress the proximity bias is by biasing the size of a mask pattern. Since the proximity bias varies with properties of a photoresist composition, specifically dissolution contrast and acid diffusion, the proximity bias of a mask varies with the type of photoresist composition. For a particular type of photoresist composition, a mask having a different proximity bias must be used. This adds to the burden of mask manufacturing. Then the pack and unpack (PAU) method is proposed in Proc. SPIE Vol. 5753, p 171 (2005), which involves strong super-resolution illumination of a first positive resist to resolve a dense hole pattern, coating the first positive resist pattern with a negative resist film material in alcohol solvent which does not dissolve the first positive resist pattern, exposure and development of an unnecessary hole portion to close the corresponding holes, thereby forming both a dense pattern and an isolated pattern. One problem of the PAU method is misalignment between first and second exposures, as the authors point out in the report. The hole pattern which is not closed by the second development experiences two developments and thus undergoes a size change, which is another problem.

To form a random pitch hole pattern by organic solvent development entailing positive/negative reversal, a mask is used in which a lattice-like pattern is arrayed over the entire surface and the width of gratings is thickened only where holes are to be formed as described in JP-A 2011-170316, paragraph [0102].

Also useful is a mask in which a lattice-like pattern is arrayed over the entire surface and thick dots are disposed only where holes are to be formed.

On use of a mask bearing no lattice-like pattern arrayed, holes are difficult to form, or even if holes are formed, a variation of mask size is largely reflected by a variation of hole size because the optical image has a low contrast.

EXAMPLE

Examples of the invention are given below by way of illustration and not by way of limitation. The abbreviation “pbw” is parts by weight. For all polymers, Mw and Mn are determined by GPC versus polystyrene standards using tetrahydrofuran solvent.

Examples and Comparative Examples Polymers

Composition, Mw and Mw/Mn

Polymers used in test compositions are identified in Table 1 with their molar fraction (mol %) of constituent recurring units, molecular weight (Mw) and dispersity (Mw/Mn). The structure of individual recurring units is shown in Tables 2 and 3. In Table 2, ALU-1 and ALU-2 correspond to recurring units (a1) having an acid labile group essential for the polymer in the inventive negative resist composition. Polymer-1 to Polymer-10 fall within the scope of the invention whereas Polymer-11 to Polymer-15 are comparative polymers.

TABLE 1 Polymer Unit 1 Fraction Unit 2 Fraction Unit 3 Fraction Unit 4 Fraction Unit 5 Fraction Mw Mw/Mn 1 ALU-1 50 Unit-1 20 Unit-2 20 Unit-5 10 9,100 1.60 2 ALU-1 50 Unit-2 40 Unit-5 10 9,000 1.75 3 ALU-1 50 Unit-1 50 8,800 1.55 4 ALU-2 50 Unit-1 30 Unit-2 20 9,500 1.60 5 ALU-1 25 ALU-3 25 Unit-1 20 Unit-2 20 Unit-5 10 8,800 1.65 6 ALU-1 25 ALU-4 25 Unit-1 20 Unit-2 20 Unit-5 10 8,700 1.65 7 ALU-1 40 ALU-5 10 Unit-1 20 Unit-2 20 Unit-5 10 9,300 1.60 8 ALU-1 25 ALU-6 25 Unit-2 40 Unit-5 10 9,000 1.75 9 ALU-2 50 Unit-1 50 9,100 1.80 10 ALU-2 50 Unit-3 50 9,500 1.70 11 ALU-4 30 ALU-7 20 Unit-2 40 Unit-5 10 7,900 1.75 12 ALU-4 30 ALU-7 20 Unit-1 20 Unit-4 20 Unit-5 10 8,300 1.70 13 ALU-6 60 Unit-2 40 9,100 1.65 14 ALU-3 50 Unit-2 50 8,100 1.65 15 ALU-8 50 Unit-2 40 Unit-5 10 9,600 1.75

TABLE 2

ALU-1

ALU-2

ALU-3

ALU-4

ALU-5

ALU-6

ALU-7

ALU-8

TABLE 3

Unit-1

Unit-2

Unit-3

Unit-4

Unit-5 Preparation of Resist Composition

Resist compositions in solution form were prepared by dissolving a polymer (identified above) and components in solvents in accordance with the formulation of Table 4 and filtering through a Teflon® filter with a pore size of 0.2 μm. Comparative resist compositions were similarly prepared in accordance with the formulation of Table 5. The structure of photoacid generators (PAG-1 to 4) is shown in Table 6. The structure of onium salts (Salt-1 to 5) is shown in Table 7. The structure of basic compounds (A-1 to 4) as quencher is shown in Table 8.

TABLE 4 Basic Polymer PAG Onium salt compound Solvent Resist (pbw) (pbw) (pbw) (pbw) (pbw) Example 1 PR-1 Polymer-1(100) PAG-1(12) A-1(2.1) PGMEA(2,700) GBL(300) 2 PR-2 Polymer-2(100) PAG-1(14) A-1(1.5) PGMEA(2,700) GBL(300) 3 PR-3 Polymer-3(100) PAG-1(8.6) Salt-1(6.7) PGMEA(2,700) GBL(300) 4 PR-4 Polymer-3(100) PAG-3(10.6) Salt-1(6.7) PGMEA(2,700) GBL(300) 5 PR-5 Polymer-4(100) PAG-2(4) Salt-1(9) PGMEA(2,700) GBL(300) 6 PR-6 Polymer-5(100) PAG-1(7) Salt-1(7) PGMEA(2,700) PAG-4(2) GBL(300) 7 PR-7 Polymer-6(100) PAG-1(8.6) Salt-1(6.7) PGMEA(2,700) GBL(300) 8 PR-8 Polymer-7(100) PAG-1(6.6) Salt-1(7) PGMEA(2,700) PAG-4(1.8) GBL(300) 9 PR-9 Polymer-8(100) PAG-1(8.6) Salt-1(6.7) PGMEA(2,700) GBL(300) 10 PR-10 Polymer-2(70) PAG-1(8.6) Salt-1(6.7) PGMEA(2,700) Polymer-4(30) GBL(300) 11 PR 11 Polymer-3(50) PAG-1(12) A-1(2.1) PGMEA(2,700) Polymer-5(50) GBL(300) 12 PR-12 Polymer-9(50) PAG-1(8.6) Salt-1(6.7) PGMEA(2,700) Polymer-10(50) GBL(300) 13 PR-13 Polymer-1(100) PAG-2(4) Salt-3(6.7) PGMEA(2,700) GBL(300) 14 PR-14 Polymer-2(100) PAG-3(12) Salt-3(6.7) PGMEA(2,700) GBL(300) 15 PR 15 Polymer-4(100) PAG-3(8) Salt-4(6.7) PGMEA(2,700) GBL(300) 16 PR-16 Polymer-4(100) PAG-4(12) Salt-1(6.7) PGMEA(2,700) GBL(300) 17 PR-17 Polymer-6(100) PAG-1(8.6) Salt-4(6.7) PGMEA(2,700) GBL(300) 18 PR-18 Polymer-8(100) PAG-3(8.6) Salt-4(6.7) PGMEA(2,700) GBL(300) 19 PR-19 Polymer-9(100) PAG-4(8.6) Salt-1(6.7) PGMEA(2,700) GBL(300) 20 PR-20 Polymer-2(100) PAG-4(8.6) Salt-2(5.3) A-2(0.6) PGMEA(2,700) GBL(300) 21 PR-21 Polymer-4(100) PAG-1(8.6) Salt-5(6.7) PGMEA(2,700) GBL(300) 22 PR-22 Polymer-6(100) PAG-1(8.6) Salt-4(6.7) PGMEA(2,700) GBL(300) 23 PR-23 Polymer-8(100) PAG-2(8.6) Salt-1(3.5) A-4(1.9) PGMEA(2,700) GBL(300) 24 PR-24 Polymer-9(100) PAG-1(8.6) Salt-1(3.5) A-3(1.9) PGMEA(2,700) GBL(300) 25 PR-25 Polymer-6(100) PAG-3(8.6) Salt-4(6.7) PGMEA(2,700) GBL(300)

TABLE 5 Basic Polymer PAG Onium salt compound Solvent Resist (pbw) (pbw) (pbw) (pbw) (pbw) Comparative 1 PR-26 Polymer-11(100) PAG-1(12) A-1(2.1) PGMEA(2,700) Example GBL(300) 2 PR-27 Polymer-12(100) PAG-1(12) Salt-1(6.7) PGMEA(2,700) GBL(300) 3 PR-28 Polymer-13(100) PAG-1(8) A-1(2.1) PGMEA(2,700) GBL(300) 4 PR-29 Polymer-14(100) PAG-2(12) A-1(2.1) PGMEA(2,700) GBL(300) 5 PR-30 Polymer-15(100) PAG-1(8.6) Salt-1(6.7) PGMEA(2,700) GBL(300) 6 PR-31 Polymer-11(100) PAG-3(12) Salt-4(6.7) PGMEA(2,700) GBL(300) 7 PR-32 Polymer-12(100) PAG-2(12) Salt-2(6.7) PGMEA(2,700) GBL(300) 8 PR-33 Polymer-13(100) PAG-4(12) Salt-4(6.7) PGMEA(2,700) GBL(300) 9 PR-34 Polymer-14(100) PAG-4(12) Salt-4(6.7) PGMEA(2,700) GBL(300) 10 PR-35 Polymer-15(100) PAG-4(12) Salt-4(6.7) PGMEA(2,700) GBL(300)

TABLE 6

PAG-1

PAG-2

PAG-3

PAG-4

TABLE 7

Salt-1

Salt-2

Salt-3

Salt-4

Salt-5

TABLE 8

A-1

A-2

A-3

A-4

Me stands for methyl.

The organic solvents in Tables 4 and 5 are shown below.

PGMEA: propylene glycol monomethyl ether acetate

GBL: gamma-butyrolactone

To all the resist compositions in Tables 4 and 5, 5.0 pbw of alkali-soluble surfactant SF-1 and 0.1 pbw of surfactant A were added.

-   Surfactant SF-1:     poly(3,3,3-trifluoro-2-hydroxy-1,1-dimethyl-2-trifluoromethylpropyl     methacrylate/1,1,1-trifluoro-2-hydroxy-6-methyl-2-trifluoromethylhept-4-yl     methacrylate) (described in JP-A 2008-122932)

-   Surfactant A:     3-methyl-3-(2,2,2-trifluoroethoxymethyl)-oxetane/tetrahydrofuran/2,2-dimethyl-1,3-propane     diol copolymer (Omnova Solutions, Inc.)

Evaluation Method and Results

On a substrate (silicon wafer), a spin-on carbon film ODL-50 (Shin-Etsu Chemical Co., Ltd.) having a carbon content of 100 wt % was deposited to a thickness of 200 nm and a silicon-containing spin-on hard mask SHB-A940 having a silicon content of 43 wt % was deposited thereon to a thickness of 35 nm. On this substrate for trilayer process, the resist composition shown in Tables 4 and 5 was spin coated, then baked on a hot plate at 100° C. for 60 seconds to form a resist film of 90 nm thick.

Using an ArF excimer laser immersion lithography scanner NSR-610C (Nikon Corp., NA 1.30, σ0.9/0.72, cross-pole opening 35 deg., azimuthally polarized illumination), exposure was performed in a varying dose through a 6% halftone phase shift mask bearing a lattice-like pattern with a pitch of 90 nm and a line width of 30 nm (on-wafer size). After the exposure, the wafer was baked (PEB) at the temperature shown in Tables 9 and 10 for 60 seconds and developed. Specifically, the developer shown in Tables 9 and 10 was injected from a development nozzle while the wafer was spun at 30 rpm for 3 seconds, which was followed by stationary puddle development for 27 seconds. The wafer was rinsed with 4-methyl-2-pentanol, spin dried, and baked at 100° C. for 20 seconds to evaporate off the rinse liquid, yielding a negative pattern.

A hole pattern resulted from image reversal by solvent development. By observation under TDSEM (CG-4000 by Hitachi High-Technologies Corp.), the size of 125 holes was measured, from which a size variation 36 was determined. DOP was determined by forming resist patterns at the effective sensitivity while changing the focus stepwise, and determining a focus range capable of affording a hole size of 50 nm±5%.

On organic solvent development, the resist compositions within the scope of the invention form patterns having improved dimensional uniformity and wide DOF.

Table 9 reports the PEB temperature, developer used, and test results for the inventive resist compositions in Table 4. Table 10 reports the PEB temperature, developer used, and test results for the comparative resist compositions in Table 5.

TABLE 9 PEB Hole size temperature variation DOF Resist (° C.) Developer (nm) (nm) Ex- 1 PR-1 90 n-butyl acetate 3.5 0.25 am- 2 PR-2 100 n-butyl acetate 3.9 0.25 ple 3 PR-3 70 n-butyl acetate 3.5 0.30 4 PR-4 100 n-butyl acetate 3.4 0.25 5 PR-5 70 n-butyl acetate 3.7 0.35 6 PR-6 90 n-butyl acetate 3.6 0.25 7 PR-7 95 n-butyl acetate 3.6 0.25 8 PR-8 85 n-butyl acetate 3.7 0.25 9 PR-9 90 n-butyl acetate 3.8 0.30 10 PR-10 90 2-heptanone 3.7 0.25 11 PR-11 100 methyl benzoate 3.5 0.25 12 PR-12 75 ethyl benzoate 4.0 0.35 13 PR-13 90 n-butyl acetate 3.8 0.25 14 PR-14 100 n-butyl acetate 3.6 0.30 15 PR-15 80 n-butyl acetate 3.8 0.30 16 PR-16 80 n-butyl acetate 4.0 0.25 17 PR-17 95 n-butyl acetate 3.6 0.25 18 PR-18 90 methyl benzoate 3.5 0.25 19 PR-19 70 ethyl benzoate 3.4 0.30 20 PR-20 100 2-heptanone 3.9 0.25 21 PR-21 80 n-butyl acetate 3.6 0.30 22 PR-22 90 n-butyl acetate 4.0 0.30 23 PR-23 90 n-butyl acetate 4.0 0.35 24 PR-24 70 n-butyl acetate 3.7 0.30 25 PR-25 90 n-butyl acetate 3.9 0.25

TABLE 10 PEB Hole size temperature variation DOF Resist (° C.) Developer (nm) (nm) Com- 1 PR-26 100 n-butyl acetate 5.0 0.15 par- 2 PR-27 100 n-butyl acetate 4.7 0.15 ative 3 PR-28 95 n-butyl acetate 5.5 0.15 Ex- 4 PR-29 95 n-butyl acetate 4.8 0.15 am- 5 PR-30 90 n-butyl acetate 5.3 0.10 ple 6 PR-31 100 n-butyl acetate 4.8 0.10 7 PR-32 100 2-heptanone 5.3 0.15 8 PR-33 95 methyl benzoate 5.9 0.15 9 PR-34 95 n-butyl acetate 5.0 0.20 10 PR-35 90 n-butyl acetate 5.2 0.15

As is evident from Tables 9 and 10, the negative pattern forming process involving the steps of applying a resist composition comprising a polymer comprising recurring units (a1) having an acid labile group and an optional acid generator onto a substrate, prebaking, exposing the resist film to high-energy radiation, PEB, and developing the exposed film in an organic solvent to form a negative pattern wherein the unexposed region is dissolved away and the exposed region is not dissolved is successful in forming hole patterns with a minimized size variation and at improved DOF.

While the invention has been described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims.

Japanese Patent Application No. 2013-012870 is incorporated herein by reference.

Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims. 

The invention claimed is:
 1. A pattern forming process comprising the steps of: applying a resist composition comprising a polymer and an optional acid generator onto a substrate, prebaking the composition to form a resist film, exposing a selected region of the resist film to high-energy radiation, baking, and developing the exposed film in an organic solvent-based developer to form a negative pattern wherein the unexposed region of resist film is dissolved away and the exposed region of resist film is not dissolved, said polymer consisting of: recurring units (a1) having an acid labile group of formula (1a), represented by the general formula (1):

wherein R¹ is methyl, and the broken line designates a valence bond, recurring units (a2) represented by the general formula (2) and recurring units of at least one type selected from recurring units (b1) to (b4) represented by the general formula (3):

wherein R¹⁰ is hydrogen or methyl, R¹¹ is an acid labile group other than formula (1a), and X¹ is a single bond, phenylene, naphthylene, or —C(═O)—O—R¹²— wherein R¹² is a straight, branched or cyclic C₁-C₁₀ alkylene group which may contain an ether radical, ester radical, lactone ring or hydroxyl radical, or a phenylene or naphthylene group,

wherein R¹³ and R¹⁶ each are hydrogen or methyl; R¹⁴ is a di- to pentavalent, straight, branched or cyclic C₁-C₁₆ aliphatic hydrocarbon group which may contain an ether or ester radical; R¹⁵ and R¹⁷ each are an acid labile group; R¹⁸ to R²¹ and R²² to R²⁵ are each independently hydrogen, cyano, a straight, branched or cyclic C₁-C₆ alkyl group, alkoxycarbonyl, or a group having an ether radical or lactone ring, at least one of R¹⁸ to R²¹ and R²² to R²⁵ has a hydroxyl group substituted with an acid labile group; m is an integer of 1 to 4, n is 0 or 1; recurring units (c) derived from a monomer having an adhesive group, but not an acid labile group, the adhesive group being selected from the group consisting of a hydroxyl, cyano, carbonyl, ester, ether, lactone ring, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone and carbonate group; recurring units of at least one type selected from recurring units (d1), (d2) and (d3) represented by the general formula:

wherein R⁰²⁰, R⁰²⁴ and R⁰²⁸ each are hydrogen or methyl, R⁰²¹ is a single bond, phenylene, —O—R⁰³³—, or —C(═O)—Y—R⁰³³—, Y is oxygen or NH, R⁰³³ is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl (—CO—), ester (—COO—), ether (—O—) or hydroxyl radical, R⁰²², R⁰²³, R⁰²⁵, R⁰²⁶, R⁰²⁷, R⁰²⁹, R⁰³⁰, and R⁰³¹ are each independently a straight, branched or cyclic C₁-C₁₂ alkyl group which may contain a carbonyl, ester or ether radical, or a C₆-C₁₂ aryl, C₇-C₂₀ aralkyl, or thiophenyl group, Z¹ is a single bond, methylene, ethylene, phenylene, fluorophenylene, —O—R⁰³²—, or —C(═O)—Z²—R⁰³²—, Z² is oxygen or NH, R⁰³² is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl, ester, ether or hydroxyl radical, M⁻ is a non-nucleophilic counter ion; recurring units (e) having a non-leaving hydrocarbon group; and recurring units (f) having an oxirane or oxetane ring, wherein 0<a1<1.0, 0≦a2<1.0, 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, 0≦a2+b1+b2+b3+b4<1.0, 0<c<1.0, 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, 0≦d1+d2+d3≦0.3, 0≦e≦0.4, and 0≦f≦0.6.
 2. The process of claim 1 wherein the resist composition comprises component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2): R¹¹⁶—SO₃ ⁻M₂ ⁺  (Z1) R¹¹⁷—COO⁻M₂ ⁺  (Z2) wherein R¹¹⁶ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of sulfonic acid, R¹¹⁷ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of carboxylic acid, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.
 3. The process of claim 2 wherein component Z is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z3) or (Z4):

wherein R¹¹⁸, R¹²⁰ and R¹²¹ each are hydrogen or trifluoromethyl, R¹¹⁹ is hydrogen, hydroxyl, a substituted or unsubstituted, straight, branched or cyclic C₁-C₂₀ alkyl group or a substituted or unsubstituted C₆-C₃₀ aryl group, p is an integer of 1 to 3, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.
 4. The process of claim 1 wherein the developer comprises at least one organic solvent selected from the group consisting of 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, methylacetophenone, propyl acetate, butyl acetate, isobutyl acetate, amyl acetate, isoamyl acetate, butenyl acetate, propyl formate, butyl formate, isobutyl formate, amyl formate, isoamyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, amyl lactate, isoamyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate.
 5. The process of claim 1 wherein the step of exposing the resist film to high-energy radiation includes KrF excimer laser lithography of wavelength 248 nm, ArF excimer laser lithography of wavelength 193 nm, EUV lithography of wavelength 13.5 nm or EB lithography.
 6. A pattern forming process according to claim 1, comprising the steps of: applying a resist composition comprising a polymer comprising recurring units (a1) having an acid labile group of formula (1a), represented by formula (1), an optional acid generator, and an organic solvent, onto a substrate, prebaking the composition to form a resist film, forming a protective film on the resist film, exposing a selected region of the resist film to high-energy radiation, baking, and applying an organic solvent-based developer to dissolve away the protective film and the unexposed region of resist film for forming a negative pattern wherein the exposed region of resist film is not dissolved.
 7. A negative pattern-forming resist composition comprising a polymer, an optional acid generator, and an organic solvent, said polymer consisting of: recurring units (a1) having an acid labile group of formula (1a), represented by the general formula (1):

 wherein R¹ is methyl, and the broken line designates a valence bond, recurring units (a2) represented by the general formula (2) and recurring units of at least one type selected from recurring units (b1) to (b4) represented by the general formula (3):

 wherein R¹⁰ is hydrogen or methyl, R¹¹ is an acid labile group other than formula (1a), and X¹ is a single bond, phenylene, naphthylene, or —C(═O)—O—R¹²— wherein R¹² is a straight, branched or cyclic C₁-C₁₀ alkylene group which may contain an ether radical, ester radical, lactone ring or hydroxyl radical, or a phenylene or naphthylene group,

 wherein R¹³ and R¹⁶ each are hydrogen or methyl; R¹⁴ is a di- to pentavalent, straight, branched or cyclic C₁-C₁₆ aliphatic hydrocarbon group which may contain an ether or ester radical; R¹⁵ and R¹⁷ each are an acid labile group; R¹⁸ to R²¹ and R²² to R²⁵ are each independently hydrogen, cyano, a straight, branched or cyclic C₁-C₆ alkyl group, alkoxycarbonyl, or a group having an ether radical or lactone ring, at least one of R¹⁸ to R²¹ and R²² to R²⁵ has a hydroxyl group substituted with an acid labile group; m is an integer of 1 to 4, n is 0 or 1; recurring units (c) derived from a monomer having an adhesive group, but not an acid labile group, the adhesive group being selected from the group consisting of a hydroxyl, cyano, carbonyl, ester, ether, lactone ring, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone and carbonate group; recurring units of at least one type selected from recurring units (d1), (d2) and (d3) represented by the general formula:

 wherein R⁰²⁰, R⁰²⁴ and R⁰²⁸ each are hydrogen or methyl, R⁰²¹ is a single bond, phenylene, —O—R⁰³³—, or —C(═O)—Y—R⁰³³—, Y is oxygen or NH, R⁰³³ is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl (—CO—), ester (—COO—), ether (—O—) or hydroxyl radical, R⁰²², R⁰²³, R⁰²⁵, R⁰²⁶, R⁰²⁷, R⁰²⁹, R⁰³⁰, and R⁰³¹ are each independently a straight, branched or cyclic C₁-C₁₂ alkyl group which may contain a carbonyl, ester or ether radical, or a C₆-C₁₂ aryl, C₇-C₂₀ aralkyl, or thiophenyl group, Z¹ is a single bond, methylene, ethylene, phenylene, fluorophenylene, —O—R⁰³²—, or —C(═O)—Z²—R⁰³², Z² is oxygen or NH, R⁰³² is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl, ester, ether or hydroxyl radical, M⁻ is a non-nucleophilic counter ion; recurring units (e) having a non-leaving hydrocarbon group; and recurring units (f) having an oxirane or oxetane ring, wherein 0<a1<1.0, 0≦a2<1.0, 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, 0≦a2+b1+b2+b3+b4<1.0, 0<c<1.0, 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, 0≦d1+d2+d3≦0.3, 0≦e≦0.4, and 0≦f≦0.6, said polymer being dissolvable in a developer selected from the group consisting of 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, methylacetophenone, propyl acetate, butyl acetate, isobutyl acetate, amyl acetate, isoamyl acetate, butenyl acetate, propyl formate, butyl formate, isobutyl formate, amyl formate, isoamyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, amyl lactate, isoamyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate.
 8. The resist composition of claim 7 wherein the resist composition comprises component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2): R¹¹⁶—SO₃ ⁻M₂ ⁺  (Z1) R¹¹⁷—COO⁻M₂ ⁺  (Z2) wherein R¹¹⁶ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of sulfonic acid, R¹¹⁷ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of carboxylic acid, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.
 9. The resist composition of claim 8 wherein component Z is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z3) or (Z4):

wherein R¹¹⁸, R¹²⁰ and R¹²¹ each are hydrogen or trifluoromethyl, R¹¹⁹ is hydrogen, hydroxyl, a substituted or unsubstituted, straight, branched or cyclic C₁-C₂₀ alkyl group or a substituted or unsubstituted C₆-C₃₀ aryl group, p is an integer of 1 to 3, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation.
 10. A pattern forming process comprising the steps of: applying a resist composition onto a substrate, prebaking the composition to form a resist film, exposing a selected region of the resist film to high-energy radiation, baking, and developing the exposed film in an organic solvent-based developer to form a negative pattern wherein the unexposed region of resist film is dissolved away and the exposed region of resist film is not dissolved, wherein the resist composition consists of: a polymer, an organic solvent, and optionally an acid generator, component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2): R¹¹⁶—SO₃ ⁻M₂ ⁺  (Z1) R¹¹⁷—COO⁻M₂ ⁺  (Z2)  wherein R¹¹⁶ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of sulfonic acid, R¹¹⁷ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of carboxylic acid, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation, a basic compound, a polymeric additive, a surfactant, a dissolution regulator, and an acetylene alcohol, wherein said polymer consists of: recurring units (a1) having an acid labile group of formula (1a), represented by the general formula (1):

 wherein R¹ is hydrogen or methyl, and the broken line designates a valence bond; recurring units (a2) represented by the general formula (2) and recurring units of at least one type selected from recurring units (b1) to (b4) represented by the general formula (3):

 wherein R¹⁰ is hydrogen or methyl, R¹¹ is an acid labile group other than formula (1a), and X¹ is a single bond, phenylene, naphthylene, or —C(═O)—O—R¹²— wherein R¹² is a straight, branched or cyclic C₁-C₁₀ alkylene group which may contain an ether radical, ester radical, lactone ring or hydroxyl radical, or a phenylene or naphthylene group,

 wherein R¹³ and R¹⁶ each are hydrogen or methyl; R¹⁴ is a di- to pentavalent, straight, branched or cyclic C₁-C₁₆ aliphatic hydrocarbon group which may contain an ether or ester radical; R¹⁵ and R¹⁷ each are an acid labile group; R¹⁸ to R²¹ and R²² to R²⁵ are each independently hydrogen, cyano, a straight, branched or cyclic C₁-C₆ alkyl group, alkoxycarbonyl, or a group having an ether radical or lactone ring, at least one of R¹⁸ to R²¹ and R²² to R²⁵ has a hydroxyl group substituted with an acid labile group; m is an integer of 1 to 4, n is 0 or 1; recurring units (c) derived from a monomer having an adhesive group, but not an acid labile group, the adhesive group being selected from the group consisting of a hydroxyl, cyano, carbonyl, ester, ether, lactone ring, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone and carbonate group; recurring units of at least one type selected from recurring units (d1), (d2) and (d3) represented by the general formula:

 wherein R⁰²⁰, R⁰²⁴ and R⁰²⁸ each are hydrogen or methyl R⁰²¹ is a single bond, phenylene, —O—R⁰³³—, or —C(═O)—Y—R⁰³³—, Y is oxygen or NH, R⁰³³ is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl (—CO—), ester (—COO—), ether (—O—) or hydroxyl radical, R⁰²², R⁰²³, R⁰²⁵, R⁰²⁶, R⁰²⁷, R⁰²⁹, R⁰³⁰, and R⁰³¹ are each independently a straight, branched or cyclic C₁-C₁₂ alkyl group which may contain a carbonyl, ester or ether radical, or a C₆-C₁₂ aryl, C₇-C₂₀ aralkyl, or thiophenyl group, Z¹ is a single bond, methylene, ethylene, phenylene, fluorophenylene, —O—R⁰³², or —C(═O)—Z²—R⁰³²—, Z² is oxygen or NH, R⁰³² is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl, ester, ether or hydroxyl radical, M⁻ is a non-nucleophilic counter ion; recurring units (e) having a non-leaving hydrocarbon group; and recurring units (f) having an oxirane or oxetane ring, wherein 0<a1<1.0, 0≦a2<1.0, 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, 0≦a2+b1+b2+b3+b4<1.0, 0<c<1.0, 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, 0≦d1+d2+d3≦0.3, 0≦e≦0.4, and 0≦f≦0.6.
 11. A negative pattern-forming resist composition consisting of: a polymer, an organic solvent, and optionally an acid generator, component Z which is an onium salt of sulfonic acid or carboxylic acid represented by the general formula (Z1) or (Z2): R¹¹⁶—SO₃ ⁻M₂ ⁺  (Z1) R¹¹⁷—COO⁻M₂ ⁺  (Z2)  wherein R¹¹⁶ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of sulfonic acid, R¹¹⁷ is a straight, branched or cyclic, monovalent hydrocarbon group of 1 to 35 carbon atoms which may contain oxygen and in which at least one carbon-bonded hydrogen may be substituted by fluorine, with the proviso that fluorine is not bonded to the carbon atom at alpha-position of carboxylic acid, and M₂ ⁺ is a counter cation having a substituent, which is sulfonium, iodonium or ammonium cation, a basic compound, a polymeric additive, a surfactant, a dissolution regulator, and an acetylene alcohol, wherein said polymer consists of: recurring units (a1) having an acid labile group of formula (1a), represented by the general formula (1):

 wherein R¹ is hydrogen or methyl, and the broken line designates a valence bond; recurring units (a2) represented by the general formula (2) and recurring units of at least one type selected from recurring units (b1) to (b4) represented by the general formula (3):

 wherein R¹⁰ is hydrogen or methyl, R¹¹ is an acid labile group other than formula (1a), and X¹ is a single bond, phenylene, naphthylene, or —C(═O)—O—R¹²— wherein R¹² is a straight, branched or cyclic C₁-C₁₀ alkylene group which may contain an ether radical, ester radical, lactone ring or hydroxyl radical, or a phenylene or naphthylene group,

 wherein R¹³ and R¹⁶ each are hydrogen or methyl; R¹⁴ is a di- to pentavalent, straight, branched or cyclic C₁-C₁₆ aliphatic hydrocarbon group which may contain an ether or ester radical; R¹⁵ and R¹⁷ each are an acid labile group; R¹⁸ to R²¹ and R²² to R²⁵ are each independently hydrogen, cyano, a straight, branched or cyclic C₁-C₆ alkyl group, alkoxycarbonyl, or a group having an ether radical or lactone ring, at least one of R¹⁸ to R²¹ and R²² to R²⁵ has a hydroxyl group substituted with an acid labile group; m is an integer of 1 to 4, n is 0 or 1; recurring units (c) derived from a monomer having an adhesive group, but not an acid labile group, the adhesive group being selected from the group consisting of a hydroxyl, cyano, carbonyl, ester, ether, lactone ring, carboxyl, carboxylic anhydride, sulfonic acid ester, disulfone and carbonate group; recurring units of at least one type selected from recurring units (d1), (d2) and (d3) represented by the general formula:

 wherein R⁰²⁰, R⁰²⁴ and R⁰²⁸ each are hydrogen or methyl R⁰²¹ is a single bond, phenylene, —O—R⁰³³—, or —C(═O)—Y—R⁰³³—, Y is oxygen or NH, R⁰³³ is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl (—CO—), ester (—COO—), ether (—O—) or hydroxyl radical, R⁰²², R⁰²³, R⁰²⁵, R⁰²⁶, R⁰²⁷, R⁰²⁹, R⁰³⁰, and R⁰³¹ are each independently a straight, branched or cyclic C₁-C₁₂ alkyl group which may contain a carbonyl, ester or ether radical, or a C₆-C₁₂ aryl, C₇-C₂₀ aralkyl, or thiophenyl group, Z¹ is a single bond, methylene, ethylene, phenylene, fluorophenylene, —O—R⁰³²—, or —C(═O)—Z²—R⁰³²—, Z² is oxygen or NH, R⁰³² is a straight, branched or cyclic C₁-C₆ alkylene group, alkenylene group or phenylene group, which may contain a carbonyl, ester, ether or hydroxyl radical, M⁻ is a non-nucleophilic counter ion; recurring units (e) having a non-leaving hydrocarbon group; and recurring units (f) having an oxirane or oxetane ring, wherein 0<a1<1.0, 0≦a2<1.0, 0≦b1<1.0, 0≦b2<1.0, 0≦b3<1.0, 0≦b4<1.0, 0≦a2+b1+b2+b3+b4<1.0, 0<c<1.0, 0≦d1≦0.3, 0≦d2≦0.3, 0≦d3≦0.3, 0≦d1+d2+d3≦0.3, 0≦e≦0.4, and 0≦f≦0.6, and said polymer is dissolvable in a developer selected from the group consisting of 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, methylacetophenone, propyl acetate, butyl acetate, isobutyl acetate, amyl acetate, isoamyl acetate, butenyl acetate, propyl formate, butyl formate, isobutyl formate, amyl formate, isoamyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, amyl lactate, isoamyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate. 